25% Glass Fiber Polyamide PA66 Heat Insulation Extrusion Material Nylon Recycling Granules
Product Details:
-PA66GF25 granules are reinforced by fiberglass. The final product performance of this raw material can meet the national standard.
-PA66GF25 granules are based on PA66 resin. Then the granules are formed by twin-screw extrusion machine after adding fiberglass, efficient flame retardants and various additives.
PA66 is copolymerization for extrusion molding. PA66 is safe and reliable with excellent stability.
The product is based on PA66 resin. It is produced by twin-screw extruder after adding glass fiber and various additives.
Polywell PA66 Granules Performance Table
| NO. | Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| | Material Properties |
| 1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| 2 | Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
| 3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| 4 | Melting point | ºC | ≥240 | ≥240 |
| 5 | Testing for tensile cracks | - | No cracks | No cracks |
| 6 | Shore hardness | - | 80±5 | 80-85 |
| 7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| 8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| 9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
| 10 | Elongation at break | % | ≥2.5 | ≥2.6 |
| 11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| 12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| 13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| 14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| 15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
Characteristic
Polyamides are among the most important and proven technical thermoplastics, known for their heat resistance, stiffness and high mechanical stability.
Polyamides can be classified into different types, with PA 6, PA 6.6 and PA 12 most established on the market. Alongside ABS and PP compounds they are among the most widely used plastics, found across several sectors including the automotive, mechanical engineering, structural and installation engineering, photovoltaics and electrical engineering industries.
Application
Specially used in thermal break strips, thermal bridge, heat insulation bar, etc.
Packaging & Delivery info
Packaging details: 25kg/bag
Delivery details: Shipped in 7-15 working days after receiving the payment.
If you are interested in our products, please feel free to contact me.
Lydia
E-mail: lydia@szpolywell.cn
Tel: +86-15601568506 (WhatsApp)
Address: Yangshe Town, Zhangjiagang City, Jiangsu Province, China.
Product Tags:
|
|
25% Glass Fiber Polyamide PA66 Heat Insulation Extrusion Material Nylon Recycling Granules Images
|